Effect of Lanthanum as a Promoter on Fe-Co/SiO2 Catalyst for Fischer-Tropsch Synthesis

Research Institute of Petroleum Industry (RIPI), Catalysis and Nanotechnology Research Division, West Blvd., Azadi Sport complex, P.O. Box 14665137, Tehran, Iran, Islamic Republic of

Received: 8 Jul 2013; Revised: 18 Nov 2013; Accepted: 1 Dec 2013; Available online: 12 Mar 2014; Published: 30 Apr 2014.
Editor(s): Istadi Istadi
Open Access Copyright (c) 2014 by Authors, Published by BCREC Group
Creative Commons License This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Fulltext View|Download

Citation Format:
Cover Image
Abstract
Iron-Cobalt catalyst is well known from both operational and economical aspects for Fischer-Tropsch synthesis. Effort to increase the efficiency of this kind of catalyst is an important research topic. In this work, the effect of lanthanum on characteristic behavior, conversion and selectivity of a Fe-Co/SiO2 Fischer-Tropsch catalyst was studied. The Fe-Co-La/SiO2 Catalysts were prepared using an incipient wetness impregnation method. These catalysts were then characterized by XRF-EDAX, BET and TPR techniques, and their performance were evaluated in a lab-scale reactor at 250ºC, H2/CO = 1.8 of molar ratio, 16 barg pressure and GHSV=600 h-1. TPR analysis showed that the addition of La lowered the reduction temperature of Fe-Co catalyst, and due to a lower temperature, the sintering of the catalyst can be mitigated. Furthermore, from the micro reactor tests (about 4 days), it was found that lanthanum promoted catalyst had higher selectivity toward hydrocarbons, and lower selectivity toward CO2. © 2014 by Authors, Published by BCREC Group. This is an open access article under the CC BY-SA License (https://creativecommons.org/licenses/by-sa/4.0)
Keywords: Fischer-Tropsch synthesis; Fe-Co catalyst; lanthanum

Article Metrics:

Article Info
Section: Original Research Articles
Language : EN
Recent articles
Effect of Lanthanum as a Promoter on Fe-Co/SiO2 Catalyst for Fischer-Tropsch Synthesis Cationic Ring Opening polymerization of ε-caprolactam by a Montmorillonite Clay Catalyst Kinetic Model of LiFePO4 Formation Using Non-Isothermal Thermogravimetric Analysis Frontmatter (Front Cover, Editorial Team, Indexing, and Table of Contents) Backmatter (Author Guideline, Publication Ethics, Copyright Transfer Agreement for Publishing Form) More recent articles
  1. Iglesia, E. (1997). Design, synthesis, and use of cobalt-based Fischer-Tropsch synthesis catalysts, Applied Catalysis A: General 161: 59-78
  2. Lili, Z., Jinlin, L.G. (2009). Effect of La2O3 on a Precipitated Iron Catalyst for Fischer-Tropsch Synthesis, Chinese Journal of Catalysis 30(7): 637-642
  3. Hemmati, M.R., Kazemeini, M., Zarkesh, J., Khorasheh F. (2012). Effect of lanthanum doping on the lifetime of Co/g-Al2O3 catalysts in Fischer-Tropsch synthesis. Journal of Taiwan Institute of Chemical Engineering 43: 704-710
  4. Duvenhage, D. D.J., Coville, N.J. (2005). Fe:Co/TiO2 bimetallic catalysts for the Fischer–Tropsch reaction Part 3: The effect of Fe:Co ratio, mixing and loading on FT product selectivity, Applied Catalysis A: General 289: 231–239
  5. Sie, S.T., Krishna, R. (1999). Fundamentals and Selection of Advanced Fischer–Tropsch Reactors. Applied Catalysis A: General 186(1-2): 55-70
  6. Roper, M., Hemmerich, R., Keim W. (1984). Fischer-Tropsch Synthesis with Heterogenized Iron-Cobalt Clusters Supported on Silica. Chemical Engineering Technology 56(2): 152-153
  7. Snel R. (1989). Catalytic Hydrogenation of Carbon Monoxide to Alkenes over Partially Degraded Iron-Cobalt Complexes. The Canadian Journal of Chemical Engineering 67(6): 992-998
  8. De la Pena O’Shea, V.A., Alvarez-Galvan, M.C., Campos-Martin, J.M., Fierro, J.L.G. (2007). Fischer–Tropsch synthesis on mono- and bimetallic Co and Fe catalysts in fixed-bed and slurry reactors. Applied Catalysis A: General 326: 65-73
  9. Sardar, A., Zabidi, N.A.M., Subbarao, D. (2011). Synthesis and Characterization of Bi-metallic Fe/Co Nanocatalyst on CNTs for Fischer-Tropsch Reaction. Journal of Nano Research 16: 9-14
  10. Bedel, L., Roger, A.C., Rehspringer, J.L., Zimmermann, Y., Kiennemann, A. (2005). La/Co0.4/Fe0.6O3-δ perovskite oxides as catalysts for Fischer-Tropsch synthesis. Journal of Catalysis 235: 279-294
  11. Wang, T., Ding, Y., Lu, Y., Zh, H., Lin, L. (2008). Influence of lanthanum on the performance of Zr-Co/activated carbon catalysts in Fischer-Tropsch synthesis. Journal of Natural Gas Chemistry 17: 153-158
  12. Cai, Z., Li, J., Liew, K., Hu, J. (2010). Effect of La2O3-dopping on the Al2O3 supported cobalt catalyst for Fischer-Tropsch synthesis. Journal of Molecular Catalysis A: General 330: 10-17
  13. Lazar, K., Reiff, W.M., Guczi L. (1986). In situ studies on supported iron-ruthenium catalysts in the Fischer-Tropsch reaction. Hyperfine Interactions 28: 871-874
  14. Iglesia, E., Soledo, S.L., Fiato, R.A., Via, G.H. (1993). Bimetallic Synergy in Cobalt-Ruthenium Fischer-Tropsch Synthesis Catalysts. Journal of Catalysis 143: 345-368
  15. Mendes, F.M.T., Noronha, F.B., Souza, C.D., Silva, A.P.M., Gaspar, A.B., Schmal, M. (2004). The effect of pressure on promoted Ru and Re-Co/Niobia catalysts in the Fischer-Tropsch synthesis. Studies in Surface Science and Catalysis 147(3): 361-366
  16. Fonseca, Y.J., Fontal, B., Reyes, M., Suárez, T., Bellandi, F., Cancines, P., Loaiza, A., Briceño, M. (2007). Hydrocarbon synthesis us-ing Iron and Ruthenium/SiO2 with Fischer-Tropsch catalysis. Avances en Quimica 2(3): 15-21
  17. Ali, S., Mohd Zabidi, M.A., Subbarao, D. (2012). Influence of Particle Size and Single-Tube Diameter on Thermal Behavior of Fischer-Tropsch Reactors. Journal of Fuel Chemical Technology 40(1): 48-53
  18. Ma, X., Sun, Q., Ying, W., Fang, D. (2009). Effects of promoters on catalytic performance of Fe-Co/SiO2 catalyst for Fischer-Tropsch synthesis. Journal of Natural Gas Chemistry 18: 354-358

Last update:

No citation recorded.

Last update:

No citation recorded.